Hot Rolled Products

Hot Rolled Products

Mild Steel serves various purpose such as making general structural, flanging & forming, Auto Components, boilers & pressure vessels, Ship Building, Oil & Gas equipments, Pipeline manufacturing, Industrial Flooring, various engineering application, fabrication of various types.

Make:

HR Coils

Thickness : 1.60 to 12 mm
Width : 900 to 2000 mm
Coil Wt : 15 to 25 MT
Grades : IS 10748 Grade I – V, IS 11513 Grade O, D, DD, EDD, IS 1079 Grade O, D, DD, EDD, IS 6240, SAIL HS LPG, SAILMA, IS 2062, IS 5986 Fe 330, 360, 410, 510, ASTM-A 36/ A569 / A570

HR Sheets

Thickness : 1.60 to 6 mm
Width : 1250 to 2000 mm
Length : 2500/5000/6300 mm
Grades : IS 2062, IS 10748 Grade I – V, IS 11513 Grade O, D, DD, EDD, IS 1079 Grade O, D, DD, EDD, SAILMA, , IS 5986 Fe 330, 360, 410, 510, ASTM-A 36/ A569 / A570

Plates

Thickness : 6 to 100 mm
Width : 1250 to 3000 mm
Length : 5000/6300/8000/12000/12500 mm (Variable lengths also available)
Grades : IS 2062, IS 10748 Grade I – V, IS 11513 Grade O, D, DD, EDD, IS 1079 Grade O, D, DD, EDD, SAILMA, , IS 5986 Fe 330, 360, 410, 510, ASTM-A 36/ A569 / A570

Chequered Plates

Thickness : 3 to 10 mm
Width : 1250 to 1500 mm
Coil Wt : 5000 mm (Variable lengths also available)
Grades : IS 3502
Pattern : Tear Drop

Applications (Hot Rolled Coils & Sheets)

Specification

Application

IS 10748/1995, Grades I, II, III, IV, V

Tube making

SAIL-WTCR, IS 11513/1985 Grades O, D, DD, EDD SAIL DRAW (EDD with CBT)

Cold reducing segment

IS 1079/1994 Grades O, D, DD, EDD

General structural applications

SAILRIM

Manufacture of cycle rims

SAE 1012

Manufacture of wheel disc and cold formed products

SAIL PROP (SAE 1020)

Manufacture of propeller shaft

SAIL PREFAB (SAE 1020 Spl.)

Manufacture of Prefabricated structures

IS 2062/2006, Grade B with Copper SAILCOR/IRSM-41/HCRS

Manufacture of corrosion resistant engineering products

SAILMA, IS 2062/2006,Grades B, C, IS 5986/1992* Fe 330, 360, 410, 510

Fabrication of engineering structurals Manufacture of Hamilton and other poles, flanging applications

Strapping quality (IRS P 41)

Strapping for packaging

SAE 1541

Manufacture of fork and spokes for two wheelers

Medium Carbon Grades (SAIL MC 40/45/50/55/60 SAE 1040, SAE 1045, SAE 1055)

Chains, hair clip, sprocket, clutch plate, hacksaw blade etc.

Medium silicon electrical steel

Manufacture of electrical equipment

IS 6240/2008

Domestic/Auto LPG Cylinders

SAIL HS LPG ( JISG 3116, EN 10120)

Export quality LPG Cylinders

SAIL FORM 34, 38, 46 (E 34, E 38, E 46/ BSK 46)

Fabrication of long & cross members for LCV, MCV and HCV

SAIL SUPER FORM 45 ( JISG 3113, SAPH 45)

Long and cross member of LCV &MCV,wheel disc, wheel rim and other structural components of passenger car

API 5L, Grades A, B, X42, X46,X 52, X 56, X 60, X 65

Manufacture of tubes & pipes mostly for oil and gas sector

Chemical Composition : IS 10748

Specification

Grade

C % max

Mn % max

P % max

S % max

Si % max

IS: 10748/1995

1

0.1

0.5

0.04

0.04

For semi killed Quality Si content shall be 0.08% max

II

0.12

0.6

0.04

0.04

III

0.16

1.2

0.04

0.04

IV

0.2

1.3

0.04

0.04

V

0.25

1.3

0.04

0.04

CE: 0.45 max for grades IV and V

CE: 0.45 max for grades IV and V

SAIL WTCR

-

0.06

0.25

0.025

0.025

0.04

Specification

Grade

C % max

Mn % max

P % max

S % max

B max

SAIL SOFT

-

0.06

0.25

0.025

0.04

30 ppm

Chemical Composition: IS 1079

Quality

Constituent, Percent, Max

 

Designation

Old Designation

Name

Carbon

Manganese

Phosphorus

Sulphur

Microalloy

 

HR0

(New)

Ordinary

0.25

1.7

0.05

0.045

-

 

HR1

O

Commercial

0.15

0.6

0.05

0.035

-

 

HR2

D

Drawing

0.1

0.45

0.04

0.035

-

 

HR3

DD

Deep Drawing

0.08

0.4

0.035

0.03

-

 

HR4

EDD

Extra Deep Drawing

0.08

0.35

0.03

0.03

-

 

HR6

(New)SAIL FORM

Micro-alloyed

0.16

1.6

0.02

0.02

0.20 Si=0.4 max

 

Notes:

  • Steel of these grades can be supplied with the addition of micro-alloying elements like Boron, Titanium, Niobium and Vanadium. The micro-alloying elements shall not exceed 0.008 percent in case of Boron and 0.20 percent in case of other elements.
  • The Nitrogen content of the steel shall not be more than 0.007 percent. For Aluminium killed or Silicon-Aluminium killed, the Nitrogen content shall not exceed 0.012 percent. This has to be ensured by the manufacturer by occasional check analysis.
  • Grade HR4 and HR5 shall be supplied in fully Aluminium killed condition or Aluminium with stabilising elements.
  • When the steel is Aluminium killed, the total Aluminium content shall not be less than 0.02 percent. When the steel is Silicon killed, the Silicon content shall not be less than 0.10 percent. When the steel is Aluminium-Silicon killed, the Silicon content shall not be less than 0.03 percent and total Aluminium content shall not be less than 0.01 percent.
  • When Copper bearing steel is required the Copper content shall be between 0.20 and 0.35 percent. In case of product analysis, the Copper content shall be between 0.17 and 0.38 percent.
  • Restricted chemistry may be mutually agreed to between the purchaser and the supplier.
  • IF denotes Interstitial Free and IF-HS denotes High Strength Interstitial Free.
  • * denotes that dual phase steel may also content Cr and Mo up to 1.0 percent.

Specification

Grade

C % max

Mn % max

P % max

S % max

Si % max

SAIL DRAW

EDD (CBT)

0.04

0.15

0.015

0.015

0.03 Al: 0.025-0.06

SAIL RIM

0.07-0.11

0.30-0.45

0.04

0.04

SAE 1012

0.10-0.15

0.30-0.60

0.03

0.035

0.10 max

SAIL PROP

SAE 1020

0.17-0.23

0.32-0.6

0.04

0.03

SAIL PREFAB

SAE 1020 spl

0.23 max

1.35 max

0.04

0.03

Nb: 0.005-0.05

Chemical Composition: IS 2062/2006

GradeDesignation

Quality

Ladle Analysis % Max C

Ladle Analysis % Max Mn

Ladle Analysis % Max S

Ladle Analysis % Max P

Ladle Analysis % Max S1

Carbon Equivalent (CE) Max

E 250

A

0.23

1.5

0.045

0.045

0.4

0.42

E 250

BR BO

0.22

1.5

0.045

0.045

0.4

0.41

E 250

C

0.2

1.5

0.04

0.04

0.4

0.39

E 300

A

0.2

1.3

0.045

0.045

0.45

0.4

E 300

BR

0.2

1.3

0.045

0.045

0.45

0.4

E 300

BO

0.2

1.3

0.045

0.045

0.45

0.4

E 300

C

0.2

1.3

0.045

0.045

0.45

0.4

E 350

A

0.2

1.5

0.045

0.045

0.45

0.42

E 350

BR

0.2

1.5

0.045

0.045

0.4

0.42

E 350

BO

0.2

1.5

0.045

0.045

0.45

0.42

E 350

C

0.2

1.5

0.045

0.045

0.45

0.42

E 410

A

0.2

1.6

0.045

0.045

0.45

0.46

E 410

BR

0.2

1.6

0.045

0.045

0.45

0.46

E 410

BO

0.2

1.6

0.045

0.045

0.45

0.46

E 410

C

0.2

1.6

0.045

0.045

0.45

0.46

E 450

A

0.22

1.6

0.045

0.045

0.45

0.48

E 450

BR

0.22

1.6

0.045

0.045

0.45

0.48

E 550

A

0.22

1.65

0.02

0.025

0.5

0.5

E 550

BR

0.22

1.65

0.02

0.025

0.5

0.5

E 600

A

0.22

1.7

0.02

0.025

0.5

0.5

E 600

BR

0.22

1.7

0.02

0.025

0.5

0.5

E 650

A

0.22

1.7

0.015

0.025

0.5

0.52

E 650

BR

0.22

1.7

0.015

0.025

0.5

0.52

 

Chemical Composition

Specification

Grade

C % max

Mn % max

P % max

S % max

Si % max

 

SAIL COR

IRSM 41

0.1

0.25-0.45

0.75-0.140

0.03

0.28-0.72

 

Cr 0.35-0.60, Ni 0.20-0.47, Cu 0.30-0.60, Al 0.03 max

Cr 0.35-0.60, Ni 0.20-0.47, Cu 0.30-0.60, Al 0.03 max

 

HCRS (Cu-P)

0.15

0.25-0.8

0.07-0.15

0.03

0.28-0.50 (Cu 0.20 min)

 

IS 5986/1992

Fe 330

0.17

1

0.045

0.045

 

*

Fe 360

0.17

1.2

0.045

0.045

 

Fe 410

0.2

1.3

0.045

0.045

 

Fe 510

0.2

1.5

0.045

0.045

 

CE 0.42 max for Fe 410 and 0.45 max for Fe 510

CE 0.42 max for Fe 410 and 0.45 max for Fe 510

 

SAIL MA

300

0.25

1.5

0.055

0.055

 

300 HI

0.2

1.5

0.04

0.04

 

350

0.25

1.5

0.04

0.04

 

350 HI

0.2

1.5

0.04

0.04

 

Nb+V+Ti 0.30% max

 

Specification

Grade

C % max

Mn % max

P % max

S % max

Si % max

Al % min

Strapping Quality

IRS P 41

0.25-0.45

1.20-1.45

0.04

0.04

0.15-0.35

SAE 1541

0.36-0.44

1.30-1.60

0.03

0.03

0.15-0.35

SAIL MC 30

0.26-0.35

0.60-0.90

0.04

0.04

0.15-0.35

0.02

SAIL MC 40

0.36-0.45

0.60-0.90

0.04

0.04

0.15-0.35

0.02

SAIL MC 45

0.41-0.50

0.60-0.90

0.04

0.04

0.15-0.35

0.02

SAIL MC 50

0.46-0.55

0.60-0.90

0.4

0.04

0.15-0.35

0.02

SAIL MC 55

0.51-0.60

0.60-0.90

0.04

0.04

0.15-0.35

0.02

SAIL MC 60

0.56-0.65

0.60-0.90

0.04

0.04

0.15-0.35

0.02

Medium Si Electrical Steel

0.05

0.4

0.025

0.025

0.30 - 1.50

IS 6240/1999

0.16

0.30 min

0.025

0.025

0.025 Al0.02 min

MAE 0.1% 0.02 (Nb| Ti| B) N <90 ppm

SAIL HS LPG JISG 3116

SG 255

0.20 max

0.30 min

0.04

0.04

-

SG 295

0.20 max

0.10 max

0.04

0.04

0.35

SAIL HS LPG EN 10120

P265NB

0.19 max

0.40 min

0.025

0.015

0.25

P310NB

0.20 max

0.70 min

0.025

0.015

0.5

Nb 0.05 max Ti 0.03.030

IS 1079

SAIL MC 30

0.26-0.35

0.60-0.90

0.04

0.04

0.15-0.35

0.02

SAIL MC 40

0.36-0.45

0.60-0.90

0.04

0.04

0.15-0.35

0.02

SAIL MC 45

0.41-0.45

0.60-0.90

0.04

0.04

0.15-0.35

0.02

SAIL MC 50

0.46-0.55

0.60-0.90

0.04

0.04

0.15-0.35

0.02

SAIL MC 55

0.51-0.60

0.60-0.90

0.04

0.04

0.15-0.35

0.02

SAIL MC 60

0.56-0.65

0.60-0.90

0.04

0.04

0.15-0.35

0.02

SAIL SUPER FORM JIS G 3113

SAPH 45/440

0.14

1.2

0.015

0.01

0.15

Nb + Ti 0.10 max for SAIL FORM Grade

API 5 L

A

0.22

0.9

0.03

0,030

B

0.26

1.2

0.03

0.03

X42

0.26

1.3

0.03

0.03

X46

0.26

1.4

0.03

0.03

X52

0.26

1.4

0.03

0.03

X56

0.26

1.4

0.03

0.03

X60

0.26

1.4

0.03

0.03

X65

0.26

1.45

0.03

0.03

X70

0.26

1.65

0.03

0.03

Nb +V + Ti < 0.15%

           

Mechanical Properties

Specification

Grade

Yield Strength MPa min

Ultimate Tensile Strength MPa min

Elongation %(Up to Above 3 mm 3 mm)

Internal diameter of bend

IS: 10748/1995

I

170

290

30

T

II

210

330

28

2T

III

240

410

25

2T

IV

275

430

20

3T

V

310

490

15

3T HRB

SAIL WTCR

35

65 max Hardness

SAIL SOFT

38

55 HRB max


IS: 1079 (Sixth Revision)

Quality Designation

Quality Old Designation

Quality Name

Tensile Strength Rm2 max MPa

Percentage Elongation after Fracture A3,4 min .t<3: Gauge length Lo=80 mm

Percentage Elongation after Fracture A3, 4 min.t<3: Gauge length Lo=50 mm

Percentage Elongation after Fracture A3,4 min.t<3: Gauge length Lo=5.65 mm

Percentage Elongation after Fracture A3,4 min.t<3: Gauge length Lo=50 mm

HR0

(New)

Ordinary

*

*

*

*

*

HR1

O

Commercial

440

23

24

28

29

HR2

D

Drawing

420

25

26

30

31

HR3

DD

Deep Drawing

400

28

29

33

34

HR4

EDD

Extra Deep Drawing

380

31

32

36

37

HR6

SAILFORM 34

YST 340

400-500

*

*

26

27

SAILFORM 38

YST 380

450-570

*

*

24

25

SAILFORM 45

YST 450

500-620

*

*

20

21

Specification

Grade

Yield Strength MPa min

Ultimate Tensile Strength MPa min

Elongation %(Up to 3 mm Above 3 mm)

Internal diameter of bend

SAIL DRAW

SAIL RIM

SAE 1012

SAIL PROP

SAE 1020

310-320

440

15

SAIL PRE FAB

SAE 1020 spl.

345 min

450 min

21

Grade Designation

Quality

Tensile Strength Rm Min Mpa

Yield Stress Min Mpa<20

Yield Stress Min Mpa 20

Yield Stress Min Mpa -40

Percentage Elongation A at Gauge Length L=5.65 VS Min >40

Internal Bend Diameter Min (See Note 2) <25

Internal Bend Diameter Min (See Note 2)>25

Charpy Impact Test(See Note 3 & 4) Temp

Charpy Impact Test(See Note 3 & 4) Min

-1

-2

-3

-4

-5

-6

-7

-8

-9

-10

-11

E-250

A

410

250

240

230

23

2t

3t

-

-

E-250

BR

410

250

240

230

23

2t

3t

RT

27

E-250

BO

410

250

240

230

23

2t

3t

0

27

E-250

C

410

250

240

230

23

2t

3t

(-)20

27

E-300

A

440

300

290

280

22

2t

-

-

-

E-300

BR

440

300

290

280

22

2t

-

RT

27

E-300

BO

440

300

290

280

22

2t

-

0

27

E-300

C

440

300

290

280

22

2t

-

(-)20

27

E-350

A

490

350

330

320

22

2t

-

-

-

E-350

BR

490

350

330

320

22

2t

-

RT

27

E-350

BO

490

350

330

320

22

2t

-

0

27

E-350

C

490

350

330

320

22

2t

-

(-)20

27

E-410

A

540

410

390

380

20

2t

-

-

-

E-410

BR

540

410

390

380

20

2t

-

RT

20

E-450

BO

570

450

430

420

20

2.5t

-

0

20

E-450

C

570

450

430

420

20

2.5t

-

(-)20

20

E-550

A

650

550

530

520

12

3.0t

-

-

-

E 600

A

730

600

580

570

12

3.5t

-

-

-

E 600

BR

730

600

580

570

12

3.5t

-

RT

15

E 650

A

780

650

630

620

12

4.0t

-

-

-

E 650

BR

780

650

630

620

12

4.0t

-

RT

15

Specification

Grade

Yield Strength MPa min

Ultimate Tensile Strength MPa

Elongation %(Up to 3 mm Above 3 mm)

Internal diameter of bend

Strapping Quality

SAE 1541

Medium Carbon

C 30

55% of UTS

500-600

21

C 40

580-680

18

C 50

660-780

13

Med Si Elec

IS 6240/12008

240

350-450

25

T

SAIL HS LPG

SG 255

255

400

JISG 3116

SG 295

295

450

26

SAIL HS LPG

P265NB

265

410-500

24

EN 10120

P310NB

310

460-550

28